陶瓷墙地砖干法造粒几何参数与坯料颗粒压缩度的关系Relationship between the Geometric Parameters of Dry Granulation Machine and the Compression Degree of Blank Particles
江竹亭;段桃;黄韩凌燕;
摘要(Abstract):
针对陶瓷墙地砖干法造粒坯料颗粒压缩度偏小的问题,借助智能粉体物性测试仪分析陶瓷干法造粒机筒体倾斜角、叶片安装高度和主轴偏心率对坯料颗粒压缩度的影响。实验结果表明:当筒体倾斜角分别为0o、15o、30o、45o、60o时,坯料颗粒压缩度依次为10.6%、11.7%、13.3%、12.1%、9.7%;当叶片安装高度分别为5 mm、10 mm、15 mm、20 mm、25 mm时,坯料颗粒压缩度依次为8.6%、10.8%、12.5%、11.3%、8.9%;当主轴偏心率分别为0、0.15、0.25、0.35、0.45时,坯料颗粒压缩度依次为9.4%、11.6%、13.7%、12.1%、10.3%。综上分析可知:当筒体倾斜角为30o、叶片安装高度为15 mm、主轴偏心率为0.25时,坯料颗粒压缩度整体最优,造粒效果最好。
关键词(KeyWords): 干法造粒;筒体倾斜角;叶片安装高度;主轴偏心率;压缩度
基金项目(Foundation):
作者(Authors): 江竹亭;段桃;黄韩凌燕;
DOI: 10.13958/j.cnki.ztcg.2019.02.001
参考文献(References):
- [1] SERANTONI M, PIANCASTELLI A, COSTA A L, et al.Improvements in the production of Yb:YAG transparent ceramic materials:Spray drying optimization[J]. Optical Materials,2012, 34(6):995-1001.
- [2] AINETO M, ACOSTA A, IGLESIAS I. The role of a coal gasification fly ash as clay additive in building ceramic[J]. Journal of the European Ceramic Society, 2006, 26(16):3783-3787.
- [3]杨辉,郭兴忠,樊先平,等.我国建筑陶瓷的发展现状及节能减排[J].中国陶瓷工业, 2009, 16(2):20-23.
- [4] TAGAWA T, YANASE A, GOTO S, et al. Ceramic anode catalyst for dry methane type molten carbonate fuel cell[J].Journal of Power Sources, 2004, 126(1–2):1-7.
- [5] ITAYA Y, OKOUCHI K, UCHIYAMA S, et al. Internal heating effect and application of microwaves with fluidization of electrically conductive particles in the ceramic drying process[J].Asia-Pacific Journal of Chemical Engineering, 2002, 10(3-4):381-400.
- [6] WU N X, BAO X, LIAO D H, et al. Analysis of temperature field on ceramic dry granulation machine[J]. Advanced Materials Research, 2014, 951:49-52.
- [7]吴南星,成飞,余冬玲,等.陶瓷干法造粒过程温度场对造粒效果的研究[J].硅酸盐通报, 2016(3):837-842.
- [8]于世超,李辉,丁松雄,等.两种不同工艺制备陶瓷砖坯体粉料的物理性能[J].硅酸盐通报, 2013(5).
- [9]王斌,郑伍魁,李辉,等.我国陶瓷墙地砖制粉工艺的进展[J].硅酸盐通报, 2015(5):1312-1319.
- [10] BAMBERGER J A, ALLEMANN R T. Economic evaluation of four types of dry/wet cooling applied to the 5-MWe Raft River geothermal power plant[J]. Technical Report, 1982.
- [11] YANAI K, HIRAI M. Radial die wall pressure during ceramic powder compression and unloading[J]. Journal of the Japan Society of Powder&Powder Metallurgy, 2000, 47(4):353-363.
- [12] PENASA M, PICCOLROAZ A, ARGANI L, et al. Integration algorithms of elastoplasticity for ceramic powder compaction[J]. Journal of the European Ceramic Society, 2014, 34(11):2775-2788.